Ultra prozirna cirkonijum keramika

Upoznavanje sa materijalom

If the content of yttrium oxide as stabilizer is appropriately increased (5 mol percent ) in zirconia ceramics, the cubic phase zirconia crystal becomes the main crystal phase of the zirconia material, so the semi-permeability is very good, so it is called "super permeable oxide". zirconium". At the same time, due to its low content of tetragonal zirconia crystals, lack of phase transformation toughening mechanism, low strength and toughness, less phase transformation occurs in the entire temperature range of sintering and cooling, and the material has almost no volume change. It is called "fully stabilized zirconia".

Ultra{0}}prozirni cirkonijum potpuno-keramički materijal lansiran 2015 koristi 5 mol posto (912 tež. posto) itrija kao stabilizator (5Y- TZP), a sadržaj glinice je manji od 0,05 težinskih posto, ili gotovo bez dodatka, i kubična faza oksidacije Sadržaj kristala cirkonijuma je više od 70 posto, sadržaj tetragonalne faze je manji od 30 posto, polu{{11 }}propusnost materijala je veoma visoka, a postižu se super-transparentne performanse (istraživanja pokazuju da TP vrijednost ultra-prozirnog cirkonijuma debljine 1,0 mm dostiže više od 35), i opća čvrstoća na savijanje oko 500600 MPa, žilavost loma 2,22,7 MPa.m1/2.

Klinička primjena

Polu-propusnost četvrte-generacije cirkonijum sve-materijala je skoro bliska onoj litijum disilikatne staklokeramike, i njegova estetika je veoma dobra, ali je njegova čvrstoća bolja od ono od staklokeramike. Uglavnom se koristi za restauraciju jednostrukih krunica i ljuskica prednjih zuba.